Copper Coated Co2 Welding Wire Er70s-6

CE ISO certificate
Sample: free
Package:
1.15kg/spool; 72 pieces/pallet
2.OEM packing
Time: Normally ready goods within 8 to 25 days
Term: CIF CNF/CFR FOB EXW
Payment: T/T, LC

Product Details

 

CO2 Gas shielded welding wire ER70S-6

 

 

Chemical Composition of Deposited Metal (%)

Element

C

Mn

Si

P

S

Cu

Standard 

0.06-0.15

1.40-1.85

0.80-1.15

≤0.025

≤0.025

≤0.50

Deposited

Metal

0.08

1.52

0.90

0.014

0.010

0.17

 
Mechanical Properties of Deposited Metal (%)

Item

Yield 

Tensile Strength       Rel/Rp0.2 MPa


Elongation A/%

Standard

≥500

≥420

≥22

Samples

560

440

30

 

Feature of Copper Coated Co2 Welding Wire Er70s-6

1.Brand:Ocean welding/DAYANG

2.Certificate: ISO9001-2008, CE,SGS

3.OEM: Acceptable

4.Package: 1kg/spool or 5kgs/spool or 15kgs/spool 

5.packaging can be changed according to your requirements

6.Sample: free, freight collect

 

Package details

1.15kg/spool; 1080kgs/pallet

2. As clients’ requirement, accept OEM

3. MOQ: 10 tons

 

Delivery: 

Time: It is about 25 days after your confirmation

Term: FOB EXW CIF CNF/CFR DDU DDP

Port: Shanghai; Ningbo; Yiwu

About us

1.We are Hangzhou Lin an Dayang Welding Material Co., Ltd., one of leading manufacturing enterprises in China,   specialized in making consumables like welding electrodes, welding wire, for 20 years. 

2.Professional production team, product line, experience technical experts who engaged in this industry  for about 20 years, We have the professional production line for welding wire now .

Compared with other welding methods, gas shielded welding has the following characteristics:

(1) The visibility of the arc and the molten pool is good, and the welding parameters can be adjusted according to the condition of the molten pool during the welding process.

(2) The welding process is easy to operate, there is no slag or very little slag, and basically no slag is needed after welding.

(3) The arc concentrates under the compression of the protective airflow, the welding speed is faster, the molten pool is smaller, the heat affected zone is narrow, and the weldment has little deformation after welding.

(4) Conducive to the mechanization and automation of the welding process, especially the mechanized welding of the spatial position.

(5) It is possible to weld magnesium, aluminum, chin and alloys thereof which are chemically active and easily form a high melting point oxide film.

(6) The thin plate can be welded.

(7) When working outdoors, a windshield device is required, otherwise the gas protection effect is not good or even poor.

(8) The optical radiation of the arc is very strong.

(9) Welding equipment is more complicated and is more expensive than electrode arc welding equipment.


Product picture of Copper Coated Co2 Welding Wire Er70s-6